ZYLAR® 550
| Category: | MMBS , Methyl Methacrylate Butadiene Styrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | ZYLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dp3ccz_ZYLAR-550.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ZYLAR 550 is an impact modified styrene acrylic copolymer that provides practical toughness, good clarity and superior processing characteristics for demanding injection molded applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 200°C/5.0 kg | 5.00 | cm³/10min | |
| 220°C/10.0 kg | 55.0 | cm³/10min | |
| Molding Shrinkage | 0.20 to 0.60 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.10 | % | |
| Equilibrium, 23°C, 50% RH | 0.050 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 60.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 28.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 50 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Flexural Stress | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
| Notched Izod Impact Strength (23°C) | 3.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 80 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 81.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 73.0 | °C | ISO 306/B50 |
| Maximum Service Temperature | 250 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.570 | ISO 489 | |
| Transmittance (550 nm) | 90.0 | % | ASTM D1003 |
| Haze | 1.5 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 180 to 210 | °C | |
| Middle Temperature | 185 to 220 | °C | |
| Front Temperature | 190 to 225 | °C | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 30.0 to 55.0 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® R200 FR10 V0 | Ravago Group | Nylon 6 | Ravamid® |
| RTP 881 TFE 10 SI 2 | RTP Company | Acetal (POM) Copolymer | RTP |
| Menzolit® SMC 0421 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| Durez® 156 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Elastron® V V251.A65.B | Elastron USA, Inc. | TPV | Elastron® V |