RTP 3483-3
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dod1A1_RTP-3483-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.010 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 24800 | MPa | ASTM D638 |
| Tensile Strength | 138 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.7 | % | ASTM D638 |
| Flexural Modulus | 20700 | MPa | ASTM D790 |
| Flexural Strength | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 640 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 282 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 8.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 332 - 366 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Injection instructions |
|---|
| The key to successfully molding this material is to start mold open cycles as soon as the screw reaches its retracted position. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Compoceran AC601 | Arakawa Chemical Industries, Ltd. | Acrylic, Unspecified | Compoceran |
| LubriOne™ NN-000/10T | PolyOne Corporation | Nylon 66 | LubriOne™ |
| Plenco 07556 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |
| SABIC® FORTIFY™ C13060D | Saudi Basic Industries Corporation (SABIC) | TPO (POE) | SABIC® FORTIFY™ |
| Durethan® AKV 30 H3.0 000000 | LANXESS GmbH | Nylon 66 | Durethan® |