Ghaed ABS ABS-38
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Ghaed Basir Petrochemicals Co. |
| Trademark: | Ghaed ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | doGGTi_Ghaed-ABS-ABS-38.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Classification: General ABS>Heat Resistance grade Characteristic: Heat Resistance grade Application: Mirror housings, Hair dryer shells, Electric oven exterior parts, Automobile parts and etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 0.35 to 0.75 | g/10 min | |
| 220°C/10.0 kg | 4.0 to 10 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 to 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 23°C) | > 43.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C) | > 16 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | > 1960 | MPa | ASTM D790 |
| Flexural Strength 4(23°C) | > 63.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5 | > 16 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 97.0 | °C | ASTM D648 |
| Vicat Softening Temperature | > 110 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 200 to 210 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 230 to 240 | °C | |
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 60.0 to 70.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 6.4mm |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ WCD841U resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |
| ALTECH® PA66 A 2030/310 GF30 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| CoREZYN® COR75-AQ-010L | Interplastic Corporation | Vinyl Ester | CoREZYN® |
| Karina WHITE PVC COMPOUND 803-10/34-A-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Perlast® ICE G75LT | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |