VAMPALLOY 0024 V0 11
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPALLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | do1n4w_VAMPALLOY-0024-V0-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V0, very good fluidity, very good surface appearance, medium chemical resistance, chlorine and bhromine free. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 | % | |
| Across Flow | 0.60 | % | |
| Water Absorption (Saturation) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 50 | % | ASTM D638 |
| Flexural Modulus | 2700 | MPa | ASTM D790 |
| Flexural Strength | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 25 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648A |
| Vicat Softening Temperature | 110 | °C | ASTM D1525 1 |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (2.00 mm) | 850 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 8750U | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Surlyn® 1601-2LM | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| Wah Hong UP WH-8100-BLK D | Wah Hong Industrial Corp. | Polyester Alloy | Wah Hong UP |
| TRIEL® 5722EM | Samyang Corporation | TPEE | TRIEL® |
| INSTRUC PPGF10GB15CC | Infinity LTL Engineered Compounds | PP, Unspecified | INSTRUC |