Retpol® PDR 9044 UVA
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dmW9yo_Retpol-PDR-9044-UVA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Retpol PDR 9044 UVA is a high flow, flame retardant copolymer polypropylene compound providing good impact strength and rigidity. The flame retardant system is based on halogenated hydrocarbon compounds with an antimony trioxide synergist. It has been UV stabilized for extended outdoor weathering. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 28 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 1.9 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 22.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 130 | % | ASTM D638 |
| Flexural Modulus | 1120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 93 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 93.0 | °C | ASTM D648 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 5 | % | |
| Processing (Melt) Temp | 180 to 225 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® N-109 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| TEREZ PA 6 7530 GF 15 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Daelim Po1y® LD-08A | DAELIM INDUSTRIAL CO., LTD. | LDPE | Daelim Po1y® |
| ICORENE® N6601 | ICO Polymers EMEA, A Division of A. Schulman | ABS | ICORENE® |
| CYCOLOY™ XCY630 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |