Lytex 4023
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Quantum Composites Inc. |
| Trademark: | Lytex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dmLloy_Lytex-4023.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lytex 4023 is a flame retarded version of Lytex 9063. Its use should be considered when a high level of flame retardency is required for the molded component. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.82 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 67 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 172 | MPa | ASTM D638 |
| Flexural Modulus | 15200 | MPa | ASTM D790 |
| Flexural Strength | 414 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 302 | °C | ASTM D648 |
| Continuous Use Temperature | 177 | °C | ASTM D794 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life (-12°C) | 26 | wk | |
| Demold Time (138°C) | 5.0 to 10 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V947 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| ZELAS® 7025 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | ZELAS® |
| Bergamid™ A70 TM-Z UV BK171 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Karina BROWN PVC COMP -E 856-36/639-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| OPNYL OP66UT 119 | Ovation Polymers Inc. | Nylon 66 | OPNYL |