Avantra® 8330
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | PMC Group Polymer Products |
| Trademark: | Avantra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dkz2vv_Avantra-8330.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Avantra® 8330 is a ignition resistant grade of high impact polystyrene offering unmatched heat resistance, high stiffness and thermal stability. It is free of polybrominated diphenylethers and meets UL94V-2 (0.057"-0.110"/1.45 mm - 2.8mm) rating. Applications: Avantra® 8330 is intended primarily for copier parts, business machine enclosures, and appliance components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| Saturation, 23°C | < 0.15 | % | |
| Equilibrium, 23°C, 50% | < 0.10 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 65 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 41.0 | MPa | |
| Break | 35.0 | MPa | |
| Tensile Elongation (Yield) | 13 | % | ASTM D638 |
| Flexural Modulus 1 | 2760 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 97.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm, Natural, Black, Solid | V-2 | ||
| 2.80 mm, Natural, Black, Solid | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP448T | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Visico™ LE4421/Ambicat™ LE4476 | Borealis AG | XLPE | Visico™ |
| LNP™ THERMOCOMP™ MFB71L compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |
| MACOMASS PP MM-PP HF 24 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |
| Sylvin 86029-90 Clear 8443 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |