| 20% talc filled and impact modified Polyamide 66/6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.28 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3700 | 1500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 55.0 | 33.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.5 | 27 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 12 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 220 | -- | °C | ISO 306/A50 |
| -- | 175 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3400 M-350 | RTP Company | LCP | RTP |
| MOSTEN GB 002 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Adell Polyamide BJ-33 Glass Reinforced High Impact | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| APEX® RE 8114 | Teknor Apex Company | PVC, Rigid | APEX® |
| LNP™ STAT-KON™ OE006A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ STAT-KON™ |