Color-in™ MA301-M
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | Color-in™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | diaRkz_Color-in-MA301-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MA301-M is extrusion a molding aesthetic resin.MA301-M is coextrusion product.MA301-M can extrusion with PVC,ASA.MA301-M has many properties:(1)a sense of metal and prepared flashing effect(2)low product scale(3)super weather resistance(4)chem-resistance(5)excellent high temperature and humidity resistance.MA301-M is mainly used in appearance items of household appliance,etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 | |
| Pencil Hardness - 500g | H |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 52.0 | MPa | ASTM D638 |
| Flexural Modulus | 2100 | MPa | ASTM D790 |
| Flexural Strength | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 83.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 170 to 180 | °C | |
| Middle Temperature | 185 to 190 | °C | |
| Front Temperature | 190 to 195 | °C | |
| Nozzle Temperature | 185 to 190 | °C | |
| Processing (Melt) Temp | 185 to 195 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 50 | rpm |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3400 FC-210 | RTP Company | LCP | RTP |
| Royalite R6000 | Spartech Plastics | PC | Royalite |
| Anjacom® R050/85S Black 91019 | Almaak International GmbH | PC+ABS | Anjacom® |
| KumhoSunny PC/ABS HAC5010G | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| PLEXIGLAS® Sheet Optical RP Studio 7D006 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |