Promyde® B30 NC100
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | NUREL, S.A. |
| Trademark: | Promyde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | diQ0Iv_Promyde-B30-NC100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Promyde B30 NC100 is a polyamide 6 fortified with nano clay technology. It is heat stabilized, lubricated and ready for injection molding. CHARACTERISTICS Promyde B30 NC100 is a polyamide 6 heat stabilized, lubricated and nucleated for fast cycle injection moulding. The incorporation of nano clay particles gives a product 20% stronger than conventional unfilled PA6, or PA66. APPLICATIONS Promyde B30 NC100 provides significant weight reduction advantages over glass filled, glass bead filled, and mineral filled PA6, and PA66. Promyde B30 NC100 processes similarly to standard unfilled PA6 and can be used in PA66 moulds. Promyde B30 NC100 is suitable for PA66 applications where temperature is not critical, as a lighter alternative to mineral filled and glass bead filled polyamides, and parts where dimensional stability is vital. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 145 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ||||
| Vertical flow direction | 0.80 - 0.90 | -- | % | |
| Flow direction | 0.70 - 0.85 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % | ISO 62 |
| Viscosity Number 1(H2SO4 (Sulphuric Acid)) | 132 | -- | cm³/g | ISO 960 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4000 | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 100 | 52.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield, 23°C | 3.5 | 25 | % | ISO 527-2/50 |
| Fracture, 23°C | 4.0 | > 25 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 3500 | 1400 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 130 | 70.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.3 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 4 | 222 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.60 | 6.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.025 | 0.25 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 20.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Back pressure: moderate |
| Note Message | |
|---|---|
| 1 . | 0,005 g/ml H2SO4 |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ASA S 210 | ROMIRA GmbH | ASA | Rotec® ASA |
| Smoothblend® PC-1200 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC | Smoothblend® |
| ASPUN™ 6835A | The Dow Chemical Company | LLDPE | ASPUN™ |
| Eastar™ DN003, Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| ALCOM® PC 740/4.14 RD1171-12LC | ALBIS PLASTIC GmbH | PC | ALCOM® PC |