LAMIGAMID® 510
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Schwartz Technical Plastic |
| Trademark: | LAMIGAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dhhnfT_LAMIGAMID-510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
|
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.40 | % | ISO 62 |
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 120 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 74.0 | MPa | ISO 527-2 |
| Fracture | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2 |
| Flexural Modulus | 3500 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 20% strain | 95.0 | MPa | ISO 604 |
| 10% strain | 88.0 | MPa | ISO 604 |
| 5% strain | 56.0 | MPa | ISO 604 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.020 - 0.080 | ASTM D1894 | |
| With steel-static | 0.24 - 0.28 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | > 4.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 74.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 255 | °C | ISO 3146 |
| CLTE - Flow (20 to 100°C) | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1050 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+12 | ohms | IEC 60093 |
| Dielectric Strength | 90 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.60 | IEC 60250 | |
| Dissipation Factor | 0.019 | IEC 60250 |
| Additional Information |
|---|
| Creep Rate Stress, DIN 53444, 1% Elongation: 27 N/mm²Creep Rate Stress, DIN 53444, 2% Elongation: >45 N/mm²Friction Wear: 0.15 µm/KmCoef of Friction, ASTM D1894, vs. Steel-Dynamic: 0.02 to 0.08Coef of Friction, ASTM D1894, vs. Steel-Static: 0.24 to 0.28Penetration Resistance, DIN 53482: 4E16 ohm-cmCreepage/leakage Resistance: Ka2Thermal Expension: 0.1 %/10°CSafe Temperature Range, short periods: 180°CSafe Temperature Range, permanent: -40° to 100°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J227T | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| SNOLEN® EP 0.49/47 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| TITANLENE® LDF 250YZ | Lotte Chemical Titan (M) Sdn. Bhd. | LDPE | TITANLENE® |
| Exxtral™ Performance Polyolefin HMU404 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Zetpol® 2010 | Zeon Corporation | NBR | Zetpol® |