VALOX™ 732E resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dh3Myx_VALOX-732E-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass/mineral reinforced, excellent thermal performance, low shrinkage and warp. Easy flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Specific Volume | 0.663 | cm³/g | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.30 to 0.40 | % | |
| Flow 2 | 0.40 to 0.60 | % | |
| Across Flow 3 | 0.60 to 0.80 | % | |
| Across Flow 4 | 0.40 to 0.60 | % | |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 5(Break) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation 6(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 7(50.0 mm Span) | 6890 | MPa | ASTM D790 |
| Flexural Strength 8(Break, 50.0 mm Span) | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 216 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 199 | °C | |
| CLTE - Flow | ASTM E831 | ||
| -40 to 40°C | 2.5E-5 | cm/cm/°C | |
| 60 to 138°C | 2.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.53 | ||
| 60 Hz | 3.53 | ||
| 1 MHz | 3.32 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 8.0E-3 | ||
| 60 Hz | 8.0E-3 | ||
| 1 MHz | 0.013 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 243 to 254 | °C | |
| Middle Temperature | 249 to 260 | °C | |
| Front Temperature | 254 to 266 | °C | |
| Nozzle Temperature | 254 to 271 | °C | |
| Processing (Melt) Temp | 254 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 1.5 to 3.2 mm |
| 2 . | 3.2 to 4.6 mm |
| 3 . | 3.2-4.6 mm |
| 4 . | 1.5 to 3.2 mm |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cheng Yu FRCV200 | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| LUVOCOM® 50-0833 | Lehmann & Voss & Co. | PC | LUVOCOM® |
| Perlast® G75B | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |
| PLUSTEK PB841 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| POCAN® B 3217 XF 000000 | LANXESS GmbH | PBT | POCAN® |