OPNYL OP66GF15
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ovation Polymers Inc. |
| Trademark: | OPNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dgy8Vg_OPNYL-OP66GF15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 66 - Glass reinforced (14 %), high tensile strength, stiffness and HDT. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.17 mm | 0.50 to 0.80 | % | |
| Across Flow : 3.17 mm | 0.60 to 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4100 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 105 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 4300 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 135 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 248 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 238 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflex GM1810BE | LyondellBasell Industries | mLLDPE | Starflex |
| Stylac™ IC39A | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| Cellophane™ 335WSZB | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Karina BROWN PVC COMPOUND 800-36/278-A-ERB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PENTALLOY BP (HV) H natural | PENTAC Polymer GmbH | Nylon 6+PP | PENTALLOY BP |