POLYTROPE® STR 1060EU-01 NATURAL
| Category: | Polyolefin, Enhanced TPO , Enhanced TPO Polyolefin |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYTROPE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dg04GT_POLYTROPE-STR-1060EU-01-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYTROPE STR 1060EU resin is a high melt strength thermoformable TPO that balances toughness and exceptionally high stiffness, enabling processors and end users to reduce product weight and improve processing efficiency without sacrificing product performance. It can be extruded in smooth or textured surfaces, or co-extruded with a POLYTROPE STR enhanced polyolefin cap resin to further customize its' durability, appearance, or feel for interior and exterior applications. The capability of POLYTROPE STR 1060EU to provide an exceptionally smooth surface in extrusion and thermoforming makes it well suited to lamination processes with decorative films. It is also easily colored and is paintable by standard TPO paint systems. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C, 24 hr, 3.18 mm) | 0.70 to 0.90 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2(Yield, 23°C) | 30.8 | MPa | ISO 527-2 |
| Tensile Strain 3(Break, 233°C) | 180 | % | ISO 527-2 |
| Flexural Modulus - Chord 4(23°C) | 4000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact - Flow | ASTM D256 | ||
| -30°C, 3.18 mm, Injection Molded | 32 | J/m | |
| 23°C, 3.18 mm, Injection Molded | 370 | J/m | |
| Instrumented Dart Impact (4°C, Total Energy, Ductile Failure) | 40.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 117 | °C | ISO 75-2/Bf |
| CLTE - Flow (-30 to 100°C) | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm, All Colors) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, 3180 µm, Thermoformed, Smooth) | 20 to 40 | ISO 2813 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Sag - 8 inch span, two point support (149°C, 3.20 mm) | 0.00 | mm | ASTM D3769 |
| Note Message | |
|---|---|
| 1 . | Method A |
| 2 . | Type 1, 50 mm/min |
| 3 . | Type 1, 50 mm/min |
| 4 . | Type 1A, 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V934 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RC Plastics RCPA66 | RC Plastics, Inc. (Div. of LNP Engineering Plastics) | Nylon 66 | RC Plastics |
| TEKNIFLEX® VM75 | Tekni-Films, a div of Tekni-Plex | Film, PVC | TEKNIFLEX® |
| VESTAMID® Care ML18 | Evonik Industries AG | Nylon 12 | VESTAMID® Care |
| RTP 799 A X 143522 EG | RTP Company | LDPE | RTP |