INEOS LLDPE LL6608LJ
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dfyGB4_INEOS-LLDPE-LL6608LJ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL6608LJ has been developed for the production of mailing film, carrier, bread and produce bags. LL6608LJ is a linear low density polyethylene copolymer containing hexene-1 as the co-monomer. It offers the following properties:
LL6608LJ offers high slip film with easy opening properties when used pure in the thickness range 30 to 70 µm. Addition of other polymers, masterbatch and pigments, or the use of other thicknesses may alter film slip and antiblock performance. If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. We recommend that you consult your Innovene technical representative for further advice on the use of LL6608LJ. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.929 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | < 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Modulus - 1% Secant (38 µm, Blown Film) | 290 | MPa | ISO 1184 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 38 µm, blown film | 14.0 | MPa | ISO 527-3 |
| TD : Yield, 38 µm, blown film | 16.0 | MPa | ISO 527-3 |
| MD : 38 µm, blown film | 50.0 | MPa | ISO 527-3 |
| TD : 38 µm, blown film | 35.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 1184 | ||
| MD : Broken, 38 µm, blown film | 750 | % | ISO 1184 |
| TD : Broken, 38 µm, blown film | 900 | % | ISO 1184 |
| Dart Drop Impact (38 µm, Blown Film) | 170 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 38.0 µm | 43.1 | kN/m | ASTM D1922 |
| TD : 38.0 µm | 255.0 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 116 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm) | 57 | ASTM D2457 | |
| Haze | 12 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 38 µm film, 2:1 blow up ratio, 230°C melt temperature. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMORUN® Z102B | Mitsubishi Chemical Performance Polymers, Inc. | TPE | THERMORUN® |
| Next ABS SG15-01NC | Next Polymers Ltd. | ABS | Next ABS |
| POLYabs SN0 | Polykemi AB | ABS | POLYabs |
| LNP™ STAT-KON™ DD0009XP compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |
| TPX® RT18XB | Mitsui Chemicals America, Inc. | PMP Copolymer | TPX® |