LNP™ COLORCOMP™ D1000 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dfaGMR_LNP-COLORCOMP-D1000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP D1000 is a compound based on Polycarbonate resin containing Unfilled Custom Color Also known as: LNP* COLORCOMP* Compound D-1000 Product reorder name: D1000 |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2450 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 67.0 | MPa | |
| Break | 61.0 | MPa | |
| Tensile Strain (Break) | 6.8 | % | ISO 527-2/50 |
| Flexural Stress | 91.0 | MPa | ISO 178 |
| Flexural Strain at Break 1 | 7.1 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 120 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 132 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 120 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.8E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 7.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAYPRENE® NB221-S4050 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| Desmovit® DP R CF20 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| ELASTOSIL® R plus 4806/20 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Kumho KBR 710S | Korea Kumho Petrochemical Co., Ltd. | PBR, Low Cis | Kumho KBR |
| Petlon Prime B1-G15-00-NT | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |