Huafon EP158N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Huafon Group Co., Ltd. |
| Trademark: | Huafon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | deIdL3_Huafon-EP158N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EP158N is a general purpose Nylon 66 resin. This resin offers a well-balanced combination of engineering properties characterized by high strength; good toughness; high impact; good flow and surface lubricity; abrasion resistance. Typical Applications EP158N is especially suitable for demanding injection molding flow properties and low temperature perforinance plus general purpose. Terminal applications mainly in machinery, electronics, electrical, instrumentation, automotive components, railway, home appliances, communications, cable ties and precision engineering products, etc., EP158N also can be used for the production of medical equipment, sporting goods, daily necessities and so on. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 86 | g/10 min | ISO 1133 |
| Particle Size | 1.40 to 2.00 | g/100 pellets | Internal Method |
| Relative Viscosity | 2.52 to 2.62 | Internal Method | |
| Water Content | < 2500 | mg/kg | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | 74.1 | MPa | ISO 527-2 |
| Tensile Strain 2(Break) | 55 | % | ISO 527-2 |
| Flexural Modulus 3 | 2650 | MPa | ISO 178 |
| Flexural Stress 4 | 98.1 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 5.9 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Annealed | 183 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 65.3 | °C | ISO 75-2/A |
| Vicat Softening Temperature 7 | 238 | °C | ISO 306/B120 |
| Peak Melting Temperature 8 | 266 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 9 | UL 94 | ||
| 1.00 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.00 mm | V-2 |
| Note Message | |
|---|---|
| 1 . | 48h/23°C/50%RH |
| 2 . | 48h/23°C/50%RH |
| 3 . | 48h/23°C/50%RH |
| 4 . | 48h/23°C/50%RH |
| 5 . | 48h/23°C/50%RH |
| 6 . | 48h/23°C/50%RH |
| 7 . | 48h/23°C/50%RH |
| 8 . | 10°C/min |
| 9 . | 48h/23°C/50%RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 ST HS PRTA011 NR365 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| ADENE OCYBG | A.D. Compound spa | PP Copolymer | ADENE |
| Honeywell PCTFE P4000LS | Honeywell | PCTFE | Honeywell PCTFE |
| POLYelast TPE HJ752 | Polykemi AB | PP+EPDM | POLYelast |
| Sylvin 5219-92 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |