Sarlink® TPV X10085B
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | deFCLw_Sarlink-TPV-X10085B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink 10000 Series are designed for low friction molding applications, requiring a low coefficient of friction against glass or painted steel. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore A, 5 sec, Injection Molded) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.30 to 0.40 | ASTM D1894 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow (100% Strain) | 3.90 | MPa | ASTM D412 |
| Tensile Strength - Across Flow (Break) | 7.60 | MPa | ASTM D412 |
| Tensile Elongation - Across Flow (Break) | 540 | % | ASTM D412 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 205 | °C | |
| Middle Temperature | 180 to 205 | °C | |
| Front Temperature | 180 to 205 | °C | |
| Nozzle Temperature | 185 to 210 | °C | |
| Processing (Melt) Temp | 185 to 210 | °C | |
| Mold Temperature | 10.0 to 55.0 | °C | |
| Back Pressure | 0.100 to 1.00 | MPa | |
| Screw Speed | 100 to 200 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8600FR | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Cevian®-V T500, T500SF | Daicel Polymer Ltd. | ABS | Cevian®-V |
| Elastron® G G100.A20.B | Elastron USA, Inc. | SEBS | Elastron® G |
| LOXIM 830 01 HBCC | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |
| LUVOCOM® 1105-7128/G | Lehmann & Voss & Co. | PEEK | LUVOCOM® |