Generic Polyester, TS
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ddlcHX_Generic-Polyester-TS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Polyester, TS This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 - 2.04 | g/cm³ | ASTM D792 |
| Apparent Density | 1.11 - 1.70 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (23°C) | 1.7E-4 - 0.26 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 - 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 59 - 88 | ASTM D2240 | |
| Barcol Hardness | 34 - 66 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 220 - 51900 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 34.3 - 80.6 | MPa | ASTM D638 |
| 23°C | 36.3 - 241 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 1.2 - 4.4 | % | ASTM D638 |
| Fracture, 23°C | 0.40 - 1.4 | % | ASTM D638 |
| Flexural Modulus (23°C) | 208 - 13900 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 68.9 - 267 | MPa | ASTM D790 |
| Yield, 23°C | 8.96 - 383 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 107 - 202 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 22 - 3200 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 210 - 470 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 32.2 - 261 | °C | ASTM D648 |
| CLTE - Flow | 6.0E-6 - 2.4E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity (23°C) | 0.27 - 0.30 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C) | 2.0 - 21 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 2.94 - 7.36 | ASTM D150 | |
| Dissipation Factor (23°C) | 6.0E-3 - 0.022 | ASTM D150 | |
| Arc Resistance | 178 - 191 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 500 - 600 | V | UL 746 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life (23°C) | 4.0 - 8.3 | min | |
| Shelf Life (23°C) | 13 - 14 | wk | |
| Demold Time | 5.0 - 41 | min |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Viscosity (23°C) | 0.45 - 2.7 | Pa·s | |
| Gel Time (23°C) | 4.0 - 28 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 151 - 160 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Polyester, TSThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 3202-70NT | Teknor Apex Company | PVC, Flexible | APEX® |
| CP PRYME® Nylon 6 N100HSL | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| Escorene™ Ultra FL 00728CC | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Polipom 100 TF2 | Poliblend S.p.a. | Acetal (POM) Copolymer | Polipom |
| ALTECH® PA66 ECO 2033/509 GF33 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |