Pearlthane® D16N98UV
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ddFKCI_Pearlthane-D16N98UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlthane® D16N98UV is a polyether-based TPU, supplied in form of transparent, colourless pellets, combining high hardness with excellent mechanical properties and good hydrolysis and microbial resistance. Pearlthane® D16N98UV is especially designed for extrusion processes. Pearlthane® D16N98UV is especially designed for extrusion of tubes (e.g. pneumatic tubing) and profiles where excellent mechanical properties at low temperature, hydrolysis and microbe resistance are required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.10 | g/cm³ | ASTM D792 |
| 20°C | 1.10 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 30.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 95 | ASTM D2240, ISO 868 | |
| Shaw D | 48 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 12.0 | MPa | ASTM D412, ISO 527 |
| 300% strain | 24.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 31.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 380 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 2 | 140 | kN/m | ASTM D624 |
| -- 3 | 140 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 4 | -48.0 | °C | ISO 11357-2 |
| Melting Temperature 5 | 188 - 198 | °C | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 195 - 210 | °C | |
| Cylinder Zone 2 Temp. | 205 - 215 | °C | |
| Cylinder Zone 3 Temp. | 215 - 225 | °C | |
| Cylinder Zone 4 Temp. | 210 - 220 | °C | |
| Die Temperature | 195 - 210 | °C |
| Extrusion instructions |
|---|
| Type: 30/25d (l/d = 25:1), Cooling: Air, Screw: 3:1, Speed: 50 rpm, Thickness Die: 0,2 mm, Pre-heating: 1h @ 100 °C (212 °F). |
| Note Message | |
|---|---|
| 1 . | @ 20°C |
| 2 . | C mould |
| 3 . | Method B |
| 4 . | 10°C/min |
| 5 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP PP HOMO 120 | Amco Polymers | PP Homopolymer | PRIMATOP |
| Zythane® 3045DH | Alliance Polymers & Services | TPU-Capro | Zythane® |
| Ghaed ABS ABS-50 | Ghaed Basir Petrochemicals Co. | ABS | Ghaed ABS |
| OmniCarb™ PC08FR510 | OMNI Plastics, LLC | PC | OmniCarb™ |
| OnForce™ LFT LF6600-5018 X2 NHFR BLACK | PolyOne Corporation | Nylon 66 | OnForce™ LFT |