ULTEM™ HU1000 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dcUdt1_ULTEM-HU1000-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. EtO and steam sterilizable. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 9.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | |||
| 24 hr | 0.25 | % | ASTM D570 |
| Saturation, 23°C | 1.3 | % | ISO 62 |
| Equilibrium, 23°C | 1.3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3580 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 110 | MPa | ASTM D638 |
| Yield | 105 | MPa | ISO 527-2/5 |
| Break 3 | 90.0 | MPa | ASTM D638 |
| Break | 85.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/5 |
| Break 5 | 60 | % | ASTM D638 |
| Break | 60 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3440 | MPa | ASTM D790 |
| -- 7 | 3300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 160 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 173 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 55 | J/m | ASTM D256 |
| 23°C | 53 | J/m | ASTM D256 |
| -30°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 201 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 215 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 219 | °C | ASTM D1525 13 |
| -- | 215 | °C | ISO 306/B50 |
| -- | 211 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -20 to 150°C | 5.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -20 to 150°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Air | 33 | kV/mm | |
| 1.60 mm, in Oil | 28 | kV/mm | |
| Dielectric Constant (1 kHz) | 3.15 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 1.3E-3 | ||
| 2.45 GHz | 2.5E-3 | ||
| Arc Resistance 14 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 47 | % | ASTM D2863 |
| NBS Smoke Density - Flaming, Ds, 4 min | 0.700 | ASTM E662 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| 14 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bayblend® T90 HT | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| BESTNYL SC00VI01AWX | Triesa Plastics | Nylon 66/6 | BESTNYL |
| ALCUDIA® HDPE R4805D1 | REPSOL | HDPE | ALCUDIA® HDPE |
| CYCOLOY™ CM8722 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| Korton FEP | Saint Gobain - Norton | PVDF | Korton |