Order Products : sales@su-jiao.com
DOW™ MDPE NG6995
| Category: | MDPE , Medium Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ MDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dcMSNG_DOW-MDPE-NG6995.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MPDE NG 6995 is a Medium Density Polyethylene Resin produced in the Gas Phase technology. It is designed for blown film applications providing good processability and seal properties. It offers good tear and impact resistance. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.939 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.38 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 11 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 19.8 | MPa | ASTM D638 |
| Fracture, molding | 33.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 1000 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 850 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| Film Puncture Resistance | 5.79 | J/cm³ | ASTM D5748 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 1130 | MPa | ASTM D882 |
| 2% secant, MD | 798 | MPa | ASTM D882 |
| 1% secant, TD | 1290 | MPa | ASTM D882 |
| 2% secant, TD | 887 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 16.0 | MPa | ASTM D882 |
| TD : Yield | 18.0 | MPa | ASTM D882 |
| MD : Fracture | 34.8 | MPa | ASTM D882 |
| TD : Fracture | 26.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 310 | % | ASTM D882 |
| TD : Fracture | 610 | % | ASTM D882 |
| Dart Drop Impact | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 10 | g | ASTM D1922 |
| TD | 270 | g | ASTM D1922 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 76 | J/m | ASTM D256 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 12 | ASTM D2457 | |
| Haze | 62 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 209 | °C |
| Extrusion instructions |
|---|
| Die Gap: 1.2 MmBlow-up Ratio: 3.6Output: 7.5 kg/hDie Temperature: 437°FMelt Temperature: 409°FTemperture Profile: 356-392-419-437°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4650-01UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| apifive® DP1171/1/270 | API SpA | Polyolefin, Unspecified | apifive® |
| DuraFlex 403-2 | Evermore Chemical Industry Co., Ltd. | TPU-Polyether | DuraFlex |
| Karina GRAY PVC COMPOUND 751-18/355-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1-0889-5 | LEHVOSS Group | Nylon 66 | LUVOCOM® |