Larton GCE/650
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Larton |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dcBEsH_Larton-GCE-650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyphenylene Sulphide (PPS). UL94 V-0 classified, halogens free. Glass fibres / Mineral filler. Product UL certified. Very good chemical resistance. Very good thermal resistance. Low smoke toxicity index and optical density. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.92 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.15 to 0.30 | % | |
| Flow : 2.00 mm | 0.10 to 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 23000 | MPa | |
| 60°C | 22000 | MPa | |
| 90°C | 21000 | MPa | |
| 120°C | 14000 | MPa | |
| 150°C | 9400 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 165 | MPa | |
| Break, 60°C | 145 | MPa | |
| Break, 90°C | 125 | MPa | |
| Break, 120°C | 105 | MPa | |
| Break, 150°C | 90.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 0.80 | % | |
| Break, 60°C | 0.90 | % | |
| Break, 90°C | 1.0 | % | |
| Break, 120°C | 1.6 | % | |
| Break, 150°C | 2.3 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 60 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 285 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 275 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 225 | °C | |
| Vicat Softening Temperature | 260 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 4.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 45 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 290 to 330 | °C | |
| Mold Temperature | 130 to 140 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9058-90UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Advanced-PP 1101P | Advanced Petrochemical Company | PP Homopolymer | Advanced-PP |
| DURANEX® SF3300 | Polyplastics Co., Ltd. | PBT | DURANEX® |
| Innova Clear R 350L G2 | Innova SA | PS (HIPS) | Innova |
| Monprene® CP-18943 CLR (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |