| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dYW70h_Rilsan-BZM-43-G9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan®BZM 43 G9 is a polyamide 11 (nylon 11) product, which contains a 43% glass fiber reinforced material. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.41 | -- | g/cm³ | ASTM D792 |
| -- | 1420 | 1420 | kg/m³ | ISO 1183 1 |
| Melt volume-flow rate (235°C/2.16 kg) | 2.00 | -- | cm³/10min | ISO 1133 2 |
| Water Absorption | ||||
| 24 hr | 0.10 | -- | % | ASTM D570 |
| Saturation | 0.50 | -- | % | ASTM D570 |
| Saturation | 1.1 | -- | % | ISO 62 3 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 111 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 8300 | MPa | ISO 527-2 4 |
| Tensile Stress | ||||
| Fracture | 146 | 143 | MPa | ISO 527-2 5 |
| Limit, 23°C | 117 | -- | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Fracture, 23°C | 5.0 | -- | % | ASTM D638 |
| Fracture | 4.0 | 4.0 | % | ISO 527-2 6 |
| Flexural Modulus (23°C) | 8270 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA 7 | |||
| -30°C | 10.0 | 10.0 | kJ/m² | ISO 179/1eA |
| 23°C | 12.0 | 12.0 | kJ/m² | ISO 179/1eA |
| Charpy impact strength | ISO 179/1eU 8 | |||
| -30°C | 75.0 | 73.0 | kJ/m² | ISO 179/1eU |
| 23°C | 67.0 | 74.0 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 80 | -- | J/m | ASTM D256 |
| 23°C | 110 | -- | J/m | ASTM D256 |
| 80°C | 200 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa | 180 | -- | °C | ISO 75-2 9 |
| 1.8 MPa, not annealed | 177 | -- | °C | ASTM D648 |
| 1.8 MPa | 175 | -- | °C | ISO 75-2 10 |
| Vicat Softening Temperature (50°C/h, B (50N)) | 180 | -- | °C | ISO 306 11 |
| Melting Temperature | ||||
| -- | 186 | -- | °C | |
| -- 12 | 189 | -- | °C | ISO 11357-3 13 |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 14 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 8.0E+12 | ohms | IEC 60093 15 |
| Volume Resistivity | -- | 4.0E+11 | ohms·m | IEC 60093 16 |
| Electric strength | -- | 22 | kV/mm | IEC 60243-1 17 |
| Comparative Tracking Index | -- | 275 | IEC 60112 18 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | -- | ISO 1210 19 | |
| Burning Behav. at thickness h (3.20 mm) | HB | -- | ISO 1210 20 | |
| Oxygen Index | 22 | -- | % | ISO 4589-2 21 |
| Additional Information |
|---|
| 干燥 Tensile Strength, Ultimate, ASTM D638, 176°F: 12,000 psiTensile Strength, Ultimate, ASTM D638, -40°F: 27,000 psiTensile Elongation, Ultimate, ASTM D638, 176°F: 10 %Tensile Elongation, Ultimate, ASTM D638, -40°F: 5 %Flexural Modulus, Tangent, ASTM D790, 176°F: 660,000 psiFlexural Modulus, Tangent, ASTM D790, -40°F: 1,400,000 psi |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | 10 °C/min |
| 13 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 14 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 15 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 16 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 17 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 18 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 19 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 20 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 21 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1003 GB 20 TFE 15 | RTP Company | PBT | RTP |
| VESTAMID® Care ML18 | Evonik Industries AG | Nylon 12 | VESTAMID® Care |
| Boltaron 1165 | Boltaron Performance Products | ABS+PVC+Acrylic | Boltaron |
| ANYPOL CL-1600F | SH Energy & Chemical | PS (EPS) | ANYPOL |
| DOW™ Electrical & Telecommunications DHDA-7700 BK | The Dow Chemical Company | TP, Unspecified | DOW™ Electrical & Telecommunications |