CYCOLOY™ C1200HF resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dYPHYf_CYCOLOYC1200HFresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLOY C1200HF is the improved version of CYCOLOY C1200 and has been developed to provide enhanced productivity and surface appearance for |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 260°C/2.16 kg | 8.00 | cm³/10min | ISO 1133 |
| 260°C/5.0 kg | 22.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 96.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5, ISO 527-2/50 | ||
| Yield | 55.0 | MPa | ISO 527-2/5, ISO 527-2/50 |
| Fracture | 45.0 | MPa | ISO 527-2/5, ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 5.0 | % | ISO 527-2/5 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture | 100 | % | ISO 527-2/5 |
| Fracture | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2300 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 63.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 3 | 18 | kJ/m² | ISO 179/1eA |
| -30°C 4 | 30 | kJ/m² | ISO 179/1eA |
| 23°C 5 | 45 | kJ/m² | ISO 179/1eA |
| 23°C 6 | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 7 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C 8 | 20 | kJ/m² | ISO 180/1A |
| -30°C 9 | 30 | kJ/m² | ISO 180/1A |
| 23°C 10 | 50 | kJ/m² | ISO 180/1A |
| 23°C 11 | 40 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C 12 | No Break | ISO 180/1U | |
| 23°C 13 | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 14 | |||
| 0.45 MPa, unannealed, 100 mm span | 128 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 108 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 132 | °C | ISO 306/B50 |
| -- | 134 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 35 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 25 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.80 | IEC 60250 | |
| 60 Hz | 2.80 | IEC 60250 | |
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 2.0E-3 | IEC 60250 | |
| 60 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 7.0E-3 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.20 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 80 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 250 - 290 | °C | |
| Middle Temperature | 255 - 295 | °C | |
| Front Temperature | 260 - 300 | °C | |
| Nozzle Temperature | 275 - 300 | °C | |
| Processing (Melt) Temp | 275 - 300 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*3 sp=62mm |
| 5 . | 80*10*4 sp=62mm |
| 6 . | 80*10*3 sp=62mm |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*3 |
| 10 . | 80*10*3 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*3 |
| 14 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE OM-1148 BLACK 404 | Teknor Apex Company | TPE | Sarlink® TPE |
| SAXAMID™ 226F5RY01 | SAX Polymers | Nylon 66 | SAXAMID™ |
| TARFLON™ SC-170 | Idemitsu Kosan Co., Ltd. | PC+ABS | TARFLON™ |
| Kotex KFN-30 | Kotec Corporation | PC | Kotex |
| MAJORIS GC163 | AD majoris | PP, Unspecified | MAJORIS |