Ultralast™ PE952
| Category: | PUR-Ether/PPDI , Polyurethane (Polyether, PPDI) |
| Manufacturer: | Chemtura |
| Trademark: | Ultralast™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dYLAuV_Ultralast-PE952.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultralast Thermoplastic Urethanes combine our proprietary LF and polymerization technology that provide well-defined molecular structure, better phase segregation and stronger hard segments. Features of Ultralast PE952 include:
MARKETS Ultralast Thermoplastic Urethanes can meet the needs of the most demanding applications. PE952 is designed but not limited to the recreational sports, industrial, mining and oil & gas markets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 | % | |
| Across Flow : 24 hr | 2.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 95 to 97 | ||
| Shore D | 43 to 45 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 89.5 | MPa | ASTM D790 |
| Abrasion Resistance - DIN | 27.0 | mm³ | DIN 53516 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Dynamic Properties | |||
| Storage Modulus : 30°C | 4.53E+8 | dynes/cm² | |
| Storage Modulus : 120°C | 2.97E+8 | dynes/cm² | |
| Tangent Delta : 30°C | 0.0250 | ||
| Tangent Delta : 120°C | 0.0380 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Trouser Tear Resistance | 67.1 | N/mm | ASTM D1938 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 12.4 | MPa | ASTM D412 |
| Tensile Strength | 36.5 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 660 | % | ASTM D412 |
| Tear Strength | |||
| Split 1 | 34 | kN/m | ASTM D470 |
| Split 2 | 35 | kN/m | ASTM D470 |
| Split | 44 | kN/m | ASTM D470 |
| Compression Set (70°C, 22 hr) | 35 | % | ASTM D395B |
| Bayshore Resilience | 63 | % | ASTM D2632 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -53.0 | °C | |
| Vicat Softening Temperature | 166 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 180 to 200 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 20.0 to 55.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 to 200 | °C | |
| Cylinder Zone 3 Temp. | 180 to 200 | °C | |
| Cylinder Zone 5 Temp. | 180 to 200 | °C | |
| Melt Temperature | 195 to 210 | °C | |
| Die Temperature | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Oil resistance, IRM #903 oil aged (3 weeks at 100°C) |
| 2 . | Acid resistance, 5% HCl aqueous solution aged (3 weeks at 85°C) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V861 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SABIC® PPcompound 7706 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Stanyl® TW200F6 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| VAMPLEN 2528 V0 CB | Vamp Tech | PP, Unspecified | VAMPLEN |
| LNP™ LUBRICOMP™ RCL34 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |