Silastic® Q7-4535

Category:	Silicone , Silicone
Manufacturer:	Dow Corning Corporation
Trademark:	Silastic®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	dXlDzn_SilasticQ74535.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Enhanced Tear Resistant (ETR) High Consistency Rubber silicone elastomers for peroxide cure APPLICATIONS SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are uncatalyzed elastomer materials designed for compounding into elastomer for part fabrication and medical devices. DESCRIPTION SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are a series of one-part uncatalyzed silicone elastomer raw materials. The addition of a peroxide catalyst is necessary to accomplish vulcanization. The resulting elastomers range in hardness from soft to firm (nominally 35 to 65, Shore A Durometer). These materials may be blended if desired to achieve intermediate hardnesses. After appropriate compounding with a peroxide catalyst, cure and post-cure, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

Message

Enhanced Tear Resistant (ETR) High Consistency Rubber silicone elastomers for peroxide cure

APPLICATIONS
SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are uncatalyzed elastomer materials designed for compounding into elastomer for part fabrication and medical devices.

DESCRIPTION
SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are a series of one-part uncatalyzed silicone elastomer raw materials. The addition of a peroxide catalyst is necessary to accomplish vulcanization.

The resulting elastomers range in hardness from soft to firm (nominally 35 to 65, Shore A Durometer). These materials may be blended if desired to achieve intermediate hardnesses.

After appropriate compounding with a peroxide catalyst, cure and post-cure, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

General Information
Features	High Gas Permeability High pressure heating resistance
Uses	Composite Medical/nursing supplies
Agency Ratings	EP Unspecified Rating ISO 10993-Part I USP Class VI
Processing Method	Composite

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.12	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	29		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (200% Strain)	0.900	MPa	ASTM D412
Tensile Strength	8.40	MPa	ASTM D412
Tensile Elongation (Break)	1000	%	ASTM D412
Tear Strength ¹	22.0	kN/m	ASTM D624

Additional Information
Values are for samples crosslinked with Perkadox PD-505.

Note Message
1 .	B mould

Resin Grade	Manufacturer	Category	Trademark
Maxelast® P3950CT	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
Pro-fax RP548N	LyondellBasell Industries	PP Random Copolymer	Pro-fax
AXELERON鈩?CS 7540 NT CPD	The Dow Chemical Company	LLDPE	AXELERON™
King Pearl® FD-SB	Loyal Chemical	PS (EPS)	King Pearl®
Alpha PVC 3006-85 CLEAR	Mexichem Specialty Compounds Inc.	PVC, Flexible	Alpha PVC