EVAL™ SP521
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dXHd4L_EVAL-SP521.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Orientability Ethylene Vinyl Alcohol Copolymer Applications: Shrink Film, Skin Packaging and thermoforming |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 1.9 | g/10 min | ISO 1133 |
| 210°C/2.16 kg | 4.1 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 38.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 65% RH | 5.9E-3 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| 20°C, 85% RH | 0.026 | cm³·mm/m²/atm/24 hr | ISO 14663-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 40.0 | °C | ISO 11357-2 |
| Melting Temperature | 187 | °C | ISO 11357 |
| Peak Crystallization Temperature | 162 | °C | ISO 11357-3 |
| Additional Information |
|---|
| Limit of Orientability, Simultaneous, Kuraray Method: 4 x 4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-GP1 | Polymer Resources Ltd. | Nylon 66 | PRL |
| Tenac™ Z3010 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| E-Pos 562 | Epocat Nederland BV | Epoxy | E-Pos |
| INTOL® 1723 | Versalis S.p.A. | SBR, Emulsion | INTOL® |
| OXPEKK® IG200 | Oxford Performance Materials, Inc. | PEKK | OXPEKK® |