A low viscosity grade for general injection molding. It was modified with talcum, and so suitable for parts requiring more reducing deformation than that of standard grade under same stress. Exhibits excellent dimensional accuracy. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.48 | g/cm³ | ASTM D792 |
| -- | 1.56 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 21 | g/10 min | ASTM D1238 |
| -- | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 2.00 mm | 1.7 | % | ASTM D955 |
| 3.00 mm | 1.7 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 62.0 | MPa | ASTM D638 |
| Yield, 23°C | 67.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break, 23°C | 8.0 | % | ASTM D638 |
| Break, 23°C | 5.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 4080 | MPa | ASTM D790 |
| 23°C | 4200 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 104 | MPa | ASTM D790 |
| 23°C | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.4 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 41 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 144 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| Melting Temperature | 165 | °C | |
| CLTE - Flow (20 to 80°C) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ AC1050 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Thermoset Plastics UR-101 | Thermoset, Lord Chemical Products | PUR, Unspecified | Thermoset Plastics |
| Andur 95-AP/Curene® 185 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Chemlon® 125 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Osterlene® PPR75CLNX | Osterman & Company | PP Random Copolymer | Osterlene® |