Order Products : sales@su-jiao.com
Somos® GP Plus 14122
| Category: | Unspecified , Unspecified |
| Manufacturer: | DSM Somos® |
| Trademark: | Somos® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dWBCcM_Somos-GP-Plus-14122.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DSM's Somos® GP Plus 14122 is a low-viscosity liquid photopolymer that produces water-resistant, durable and accurate three-dimensional parts. Somos® GP Plus 14122 has a white, opaque appearance with performance that mirrors production plastics like ABS and PBT. Applications Somos® GP Plus 14122 is ideal for many applications in the automotive, aerospace and consumer product industries. Somos® GP Plus 14122 is successful in creating functional prototypes, humidity / water-resistant concept models, and durable low volume production parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | |
| Water Absorption (Equilibrium) | 0.40 | % | ASTM D570 |
| Viscosity (30°C) | 340 | mPa·s |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Critical Exposure | 13.0 | mJ/cm² | |
| Penetration Depth | 158.8 | µm | |
| Puncture Energy - High Speed Puncture-Impact | 4.60 | J | ASTM D3763 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 79 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2370 to 2650 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 47.2 to 47.6 | MPa | |
| Break | 33.8 to 40.2 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 6.0 to 9.0 | % | |
| Flexural Modulus | 2180 to 2220 | MPa | ASTM D790 |
| Flexural Strength | 66.8 to 67.8 | MPa | ASTM D790 |
| Poisson's Ratio | 0.41 | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 23 to 29 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 46.0 | °C | |
| 1.8 MPa, Unannealed | 41.0 | °C | |
| Glass Transition Temperature | 41.0 to 43.0 | °C | ASTM E1545 |
| CLTE - Flow | ASTM E831 | ||
| -40 to 0°C | 6.3E-5 | cm/cm/°C | |
| 0 to 50°C | 8.9E-5 | cm/cm/°C | |
| 50 to 100°C | 1.7E-4 | cm/cm/°C | |
| 100 to 150°C | 1.7E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.80 | ||
| 1 kHz | 3.70 | ||
| 1 MHz | 3.40 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYNE® Olefins W6424 | Tyne Plastics LLC. | PP Copolymer | TYNE® Olefins |
| AKROMID® B3 GF 50 9 RM-M black (3147) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| DIC.PPS FZ-3600 | DIC Corporation | PPS | DIC.PPS |
| Hyundai EP PA66 LD260 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| NYLOY® AT-0060N | Nytex Composites Co., Ltd. | PS (GPPS) | NYLOY® |