Plantic® WR700
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | Plantic Technologies Limited |
| Trademark: | Plantic® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dUPkaV_Plantic-WR700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plantic Technologies Limited develops and produces advanced bio-based materials. Plantic® is an innovative product made from corn-starch (maize) that is Australian grown and non-genetically modified. Plantic® is an Australian registered trademark of Plantic Technologies Limited. Plantic® WR700 is a thermoplastic starch (TPS) polymer formulated for injection molding. It has been designed to be used in applications requiring water resistance for periods of up to 12 weeks. It is suitable for molding parts with a wall thickness between 0.5 - 3.0 mm. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 630 | MPa | ASTM D638 |
| Tensile Strength (Yield) | < 7.50 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 31 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 44.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 70.2 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 2.0 to 3.0 | % | |
| Rear Temperature | 110 to 150 | °C | |
| Middle Temperature | 150 to 170 | °C | |
| Front Temperature | 160 to 180 | °C | |
| Nozzle Temperature | 170 to 190 | °C | |
| Processing (Melt) Temp | 175 to 200 | °C | |
| Mold Temperature | 25.0 to 50.0 | °C | |
| Back Pressure | 0.00 to 10.0 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS VP-2 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| Clariant Nylon 6/6 PA-111G33C | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| DOMAMID® 66G30V0AH | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Sylvin 86026-80LG Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ Lexan_WR5210R compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |