LNP™ THERMOCOMP™ KZ002 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dUGQIU_LNP-THERMOCOMP-KZ002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP KZ002 is a compound based on Acetal containing 10% Milled Glass. Also known as: LNP* THERMOCOMP* Compound KF-1002 M Product reorder name: KZ002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.18 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.26 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3630 | MPa | ASTM D638 |
| -- | 3420 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Break 3 | 53.0 | MPa | ASTM D638 |
| Break | 54.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 9.6 | % | ASTM D638 |
| Yield | 10 | % | ISO 527-2/5 |
| Break 5 | 19 | % | ASTM D638 |
| Break | 21 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2770 | MPa | ASTM D790 |
| -- 7 | 2950 | MPa | ISO 178 |
| Flexural Stress | 74.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 42 | J/m | ASTM D256 |
| 23°C 8 | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 820 | J/m | ASTM D4812 |
| 23°C 9 | 49 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.10 | J | ASTM D3763 |
| -- | 1.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 153 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 101 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 153 | °C | ISO 75-2/Af |
| 1.8 MPa, Annealed, 3.20 mm | 103 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.1E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex SP-0180 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| TUFNYL® SXXIC NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| Xuchuan XCW-8750H-6 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Mylar® D1 (300 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| LUVOCOM® 80-7917 VP | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |