Daelim Po1y® XP3200
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dU3z7d_DaelimPo1yXP3200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daelim Po1y®XP3200 is a metallocene linear low density polyethylene product,. It is available in Europe or Asia Pacific. Daelim Po1y®XP3200 applications include bags/linings, movies, agriculture, food contact applications and coating applications. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 59.8 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 48.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 550 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 590 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 150 | g | ASTM D1709A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ASTM D1004 | ||
| Lateral flow : 0.0300mm | 127 | kN/m | ASTM D1004 |
| Traffic : 0.0300mm | 125 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 107 | °C | ASTM D1525 |
| Peak Melting Temperature | 115 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 89 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 18 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ML-1150DN | Teknor Apex Company | TPE | Sarlink® TPE |
| Stat-Tech™ PP-16CP/000 2 HI BLACK | PolyOne Corporation | PP, Unspecified | Stat-Tech™ |
| Sylvin 8200-55UV Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Huafon HF-1385A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| LETOXIT PR 217 | 5M s.r.o. | Epoxy | LETOXIT |