Order Products : sales@su-jiao.com
TAISOX 6634F
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dToUiT_TAISOX-6634F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 6634F is a low density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is injection molding. The main features of TAISOX 6634F are:
The typical application fields of TAISOX 6634F are: movies |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 10.8 | MPa | ASTM D638 |
| Fracture | 11.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 500 | % | ASTM D638 |
| Flexural Modulus | 186 | MPa | ASTM D790 |
| Coefficient of Friction (Blown Film) | 0.12 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Film Thickness - Recommended / Available | 0.4-2 mil (10-50 µ) | ||
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 30 µm, blown film | 177 | MPa | ASTM D882 |
| 1% secant, TD : 30 µm, blown film | 206 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 9.81 | MPa | ASTM D882 |
| TD : Yield, 30 µm, blown film | 10.8 | MPa | ASTM D882 |
| MD : Broken, 30 µm, blown film | 15.7 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 13.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 280 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 500 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 65 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, blown film | 240 | g | ASTM D1922 |
| TD : 30 µm, blown film | 1900 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 92.0 | °C | ASTM D1525 |
| Melting Temperature | 112 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 90 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film extrusion preparation parameters: Screw: 60 mm L/D: 30 Blow up ratio: 2.5 Temperature160 to 200°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 66 Industrial Series PG15-02BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Industrial Series |
| Bergamid™ B700 G15 H GREY VN 845/2 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Ferro PP TPP30AE39BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Eastar™ DN003, Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| Kumho ABS H2938 | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |