Bayblend® FR411 MT
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Bayblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dTnhaO_BayblendFR411MT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Rubber modified PC blend; flame retardant; mineral filled ; Vicat/B 120 temperature = 99 °C; extrusion grade for European railway interiors requiring EN45545; the classifications according to the respective rail standards are communicated with email inquiry under plastics@covestro.com |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.36 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Lateral flow : 3.00mm | 0.20 - 0.40 | % | ISO 2577 |
| Traffic : 3.00mm | 0.30 - 0.50 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5250 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 67.0 | MPa | ISO 527-2/50 |
| Fracture, 23°C | 59.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 3.0 | % | ISO 527-2/50 |
| Fracture, 23°C | 5.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 6.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 43 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 93.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 87.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 97.0 | °C | ISO 306/B50 |
| -- | 99.0 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 4.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 39 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.20 | IEC 60250 | |
| 23°C, 1 MHz | 3.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 6.1E-5 | IEC 60250 | |
| 23°C, 1 MHz | 7.6E-3 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm, Bayer Test | V-0 | UL 94 | |
| 1.5 mm, Bayer Test | V-0 | UL 94 | |
| 3.0 mm, Bayer Test | 5VB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 2 | 240 | Pa·s | ISO 11443-A |
| Note Message | |
|---|---|
| 1 . | 150x105x3 mm |
| 2 . | 1000/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| LEXAN™ EXL1433T resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ THERMOCOMP™ LF006E compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |
| Plenco 02571 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |
| Celanex® 3201 | Celanese Corporation | PBT | Celanex® |
| Sylvin 8887-95 Brown 7400 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |