LEXAN™ 135 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dTZuyz_.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
General purpose low flow polycarbonate powder grade |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ASTM D570 | ||
| Equilibrium, 23°C | 0.35 | % | ASTM D570 |
| Equilibrium, 100°C | 0.58 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 62.0 | MPa | ASTM D638 |
| Fracture | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 70 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 93.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 910 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 | |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 64.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 137 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 132 | °C | ASTM D648 |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 5 |
| CLTE - Flow (-40 to 95°C) | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1250 | J/kg/°C | ASTM C351 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 299 - 321 | °C | |
| Middle Temperature | 310 - 332 | °C | |
| Front Temperature | 321 - 343 | °C | |
| Nozzle Temperature | 316 - 338 | °C | |
| Processing (Melt) Temp | 321 - 343 | °C | |
| Mold Temperature | 82.2 - 116 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PE LT033 (Film Extrusion) | Sasol Polymers | LDPE | Sasol Polymers PE |
| Adell PP RQ-16 | Adell Plastics, Inc. | PP Copolymer | Adell PP |
| Caltex PP MB71 | GS Caltex | PP, Unspecified | Caltex PP |
| LUVOCOM® 1106-8465 | LEHVOSS Group | PEI | LUVOCOM® |
| WELLAMID Nylon 6000 GV 30 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |