Reny® 1371 is a Polyarylamide (PARA) material filled with 55% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® 1371 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.66 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.11 | % | |
| Equilibrium, 23°C, 50% RH | 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20800 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 242 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2 |
| Flexural Modulus | 19600 | MPa | ISO 178 |
| Flexural Stress | 403 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 93 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 236 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 227 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| -- | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN0320SN | Ginar Technology Co., LTD. | Nylon 6 | Mapex |
| SABIC® PPcompound 2605 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| KumhoSunny PBT/ABS HAB8740 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+PBT | KumhoSunny PBT/ABS |
| Hostacom G3 N01 L303613 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| RTP 199 X 141399 B | RTP Company | PP, Unspecified | RTP |