DIC.PPS ZL-130
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dTN6WD_DIC-PPS-ZL-130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DIC.PPS ZL-130 is a polyphenylene sulfide (PPS) product, which contains 30% ptfe fiber. It can be processed by injection molding and is available in North America or Asia Pacific. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.0 | % | ASTM D955 |
| Transverse flow | 1.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3700 | MPa | ASTM D638 |
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 3400 | MPa | ASTM D790 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Compressive Strength | 70.0 | MPa | ASTM D695 |
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.20 | ASTM D1894 | |
| With metal-static | 0.20 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 70 | J/m | ASTM D256 |
| Unnotched Izod Impact | 500 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 200 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 110 | °C | ASTM D648 |
| CLTE - Flow (-30 to 100°C) | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Flexural Elongation @ Break, ASTM D790: 6% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 300 - 340 | °C | |
| Middle Temperature | 300 - 340 | °C | |
| Front Temperature | 300 - 340 | °C | |
| Mold Temperature | 120 - 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pomalux® CN-SS | Westlake Plastics Company | Acetal (POM) Copolymer | Pomalux® |
| TRIBOCOMP® PA66 GF30 TS0 | EPIC Polymers | Nylon 66 | TRIBOCOMP® |
| NOVADURAN® 5010GN6-15T | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| K-vinyl 70 Deg C Rating Insulation (85-Dry) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| LEXAN™ ML6411 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |