Xuchuan 6160/B-8260 (Sole)
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Xuchuan Chemical (Suzhou) Co., Ltd |
| Trademark: | Xuchuan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dSrR5l_Xuchuan-6160-B-8260-Sole-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Xuchuan 6160/B-8260 (Sole) is a Polyurethane product. It is available in Asia Pacific. Typical application: Consumer Goods. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.900 to 1.10 | g/cm³ | |
| Density | |||
| A-6160 : 40°C | 1.010 to 1.020 | g/cm³ | |
| B-8260 : 40°C | 1.080 to 1.200 | g/cm³ | |
| Viscosity | |||
| A-6160 : 40°C | 1.00 to 1.40 | Pa·s | |
| B-8260 : 40°C | 0.700 to 1.10 | Pa·s |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Ross Flex (-20°C) 1 | No Crack | ||
| Williams Abrasion | 60.0 to 100 | cc/php |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Cream Time | 6.0 to 8.0 | sec | |
| End of Rise Time | 40.0 to 50.0 | sec |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Adhesion Strength - Between sole and mid-sole | 39.2 to 58.8 | kN/m | |
| Free Rise Foam Density | 470 to 500 | kg/m³ | |
| Preheat Temperature | |||
| Part A | 50 to 60 | °C | |
| Part B | 50 to 60 | °C | |
| Preheat Time | |||
| Part A | 8.0 to 10.0 | hr | |
| Part B | 8.0 to 12.0 | hr | |
| Processing Temperature | |||
| Part A | 40 to 45 | °C | |
| Part B | 40 to 45 | °C |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 to 70 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Break) | 9.00 to 12.0 | MPa | |
| Tensile Elongation (Break) | 600 to 720 | % | |
| Tear Strength | 29.0 to 42.0 | kN/m |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 64 to 66 | ||
| Demold Time | 5.0 to 7.0 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 45.0 to 55.0 | °C |
| Note Message | |
|---|---|
| 1 . | 100000 cycles |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ PTFE TF 2029Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| Axiall PVC 8906 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| LNP™ THERMOCOMP™ RC006XXC compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Sylvin 4200-88UV Yellow 4192 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ KONDUIT™ OX11315 compound | SABIC Innovative Plastics Asia Pacific | PPS | LNP™ KONDUIT™ |