Generic Nylon 66 - Mineral
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dSafIk_Generic-Nylon-66---Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.28 - 1.52 | g/cm³ | ASTM D792 |
| 23°C | 1.23 - 1.50 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/0.325 kg) | 2.9 - 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.40 - 1.2 | % | ASTM D955 |
| Transverse flow : 23°C | 0.98 - 1.2 | % | ASTM D955 |
| 23°C | 0.68 - 1.4 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.50 - 0.82 | % | ASTM D570 |
| 23°C, 24 hr | 0.27 - 1.3 | % | ISO 62 |
| Saturated, 23°C | 1.5 - 7.5 | % | ASTM D570 |
| Saturated, 23°C | 4.9 - 7.2 | % | ISO 62 |
| Equilibrium, 23°C | 0.30 - 2.3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.60 - 2.4 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 89 - 123 | ASTM D785 | |
| 23°C | 85 - 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3220 - 8330 | MPa | ASTM D638 |
| 23°C | 3050 - 10100 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 53.7 - 131 | MPa | ASTM D638 |
| Yield, 23°C | 58.0 - 91.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 70.8 - 132 | MPa | ASTM D638 |
| Fracture, 23°C | 57.9 - 142 | MPa | ISO 527-2 |
| 23°C | 54.7 - 95.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.8 - 4.0 | % | ASTM D638 |
| Yield, 23°C | 1.4 - 15 | % | ISO 527-2 |
| Fracture, 23°C | 1.7 - 16 | % | ASTM D638 |
| Fracture, 23°C | 1.3 - 11 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2640 - 8500 | MPa | ASTM D790 |
| 23°C | 3100 - 9140 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 99.3 - 159 | MPa | ASTM D790 |
| 23°C | 88.3 - 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 - 7.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 5.0 - 62 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 26 - 72 | J/m | ASTM D256 |
| 23°C | 2.0 - 7.9 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 45 - 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 224 - 260 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 209 - 251 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 78.4 - 245 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 76.1 - 250 | °C | ISO 75-2/A |
| Continuous Use Temperature | 80.0 - 130 | °C | ASTM D794 |
| Vicat Softening Temperature | 200 - 246 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 254 - 265 | °C | |
| -- | 250 - 263 | °C | ISO 11357-3 |
| -- | 254 - 260 | °C | ASTM D3418 |
| -- | 260 - 261 | °C | ISO 3146 |
| Linear thermal expansion coefficient | |||
| Flow | 7.2E-6 - 6.1E-5 | cm/cm/°C | ASTM D696 |
| Flow | 6.0E-6 - 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.3E-6 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 104 - 120 | °C | UL 746 |
| RTI Imp | 65.0 - 120 | °C | UL 746 |
| RTI | 104 - 115 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 - 2.5E+14 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+8 - 1.1E+17 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+14 - 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 3.5 - 24 | kV/mm | ASTM D149 |
| 23°C | 19 - 86 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.40 - 3.90 | ASTM D150 | |
| 23°C | 3.61 | IEC 60250 | |
| Dissipation Factor (23°C) | 0.010 - 0.015 | IEC 60250 | |
| Comparative Tracking Index | 300 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | |||
| -- | 27 - 28 | % | ASTM D2863 |
| -- | 24 - 34 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.3 - 90.3 | °C | |
| Drying Time | 2.8 - 5.3 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 22 | % | |
| Rear Temperature | 264 - 300 | °C | |
| Middle Temperature | 269 - 294 | °C | |
| Front Temperature | 270 - 299 | °C | |
| Nozzle Temperature | 276 - 288 | °C | |
| Processing (Melt) Temp | 263 - 299 | °C | |
| Mold Temperature | 69.3 - 101 | °C | |
| Injection Pressure | 68.7 - 97.7 | MPa | |
| Holding Pressure | 45.9 - 75.4 | MPa | |
| Back Pressure | 0.172 - 1.27 | MPa | |
| Screw Speed | 45 - 75 | rpm | |
| Cushion | 4.76 - 4.77 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 803 Z DEL | RTP Company | Acetal (POM) Copolymer | RTP |
| SCLAIR® 31G | NOVA Chemicals | LLDPE | SCLAIR® |
| CoREZYN® COR31-DA-208 | Interplastic Corporation | Polyester, TS | CoREZYN® |
| LNP™ THERMOCOMP™ UC006XXH compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| Hostacom TRC 452N G72758 | LyondellBasell Industries | PP Copolymer | Hostacom |