SLOVAMID® 6 NG GF 20
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dQqQgg_SLOVAMID-6-NG-GF-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6 for injection moulding, chemically strengthened with 20% glass fibre. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and consumer-goods industry, eg.: grips for electro tools, hobby tools, gears, cases of the electrotools, cooling skrews of blowers, electromotors, carrying parts in the automotive industry. With the increasing content of GF also the toughness, bending and tensile strength increase as well as the heat application increases up to 250°C and the shrinkage decreases. Delivered in natural mode and in the full RAL colour scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.4 | % | |
| Flow | 0.68 | % | |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 5800 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 200 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 200 | °C | ISO 306/B |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene ECHPCC40 | Rainmaker Polymers LLC | PP Homopolymer | Rainmaker Polypropylene |
| Ranger PBT PBT-201-G15 291 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| T-Blend® 5531N-SI | TSRC Corporation | TPE | T-Blend® |
| TOTAL Polyethylene LDPE 1700 MN 18 C | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| CEPLA CW-452E | CEPLA Co., LTD | PP, Unspecified | CEPLA |