Delrin® Stock Shapes AF Blend
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Ensinger Inc. |
| Trademark: | Delrin® Stock Shapes |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dQV90H_Delrin-Stock-Shapes-AF-Blend.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ensinger's DELRIN® 100AF blend stock shapes are a 13% PTFE fiber filled homopolymer acetal. They offer an improved coefficient of friction, better lubricity, and improved wear characteristics over unfilled and PTFE powder filled acetals.This advanced acetal material uses a combination of PTFE fibers uniformly dispersed in Delrin acetal resin. The combination results in improved wear characteristics along with strength, toughness, dimensional stability and machinability. The materials exceptional wear properties and internal lubrication serves to reduce or elimanate the need for external lubricants. Ensinger can also produce a full strength 20% PTFE filled version. DELRIN® 100AF is often used for applications such as bearing, bushings, cams and other antifriction devices that also require extra toughness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 77 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2360 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 54.2 | MPa | ASTM D638 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 168 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 118 | °C | ASTM D648 |
| Peak Melting Temperature | 175 | °C | ASTM D3418 |
| Service Temperature | |||
| Intermittent | 149 | °C | |
| Long Term | 85 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Data obtained from extruded shapes material. |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 504 | Marco Polo International, Inc. | HDPE | MARPOL® |
| Andur 8-3 APLF | Anderson Development Company | PUR-Ester/TDI | Andur |
| Estane® ETE 55DS3 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| Fainplast PVC RKS 430/W-OM | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Karina BLUE COLOR CONCENTRATE 06/671-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |