TAIRISAN NF2100
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRISAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dQM7un_TAIRISAN-NF2100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC SAN resin NF2100 meets the requirements of SGS and the certificates of environmental protection. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.06 | g/cm³ | ASTM D792 |
| 23°C | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 200°C/5.0 kg | 5.0 | g/10 min | |
| 220°C/10.0 kg | 50 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 23°C) | 78 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 68.6 | MPa | ASTM D638 |
| 23°C | 69.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 3430 | MPa | ASTM D790, ISO 178 |
| Flexural Strength (23°C) | 118 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.35 mm) | 15 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 92.0 | °C | ASTM D648, ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 210 to 250 | °C | |
| Middle Temperature | 210 to 250 | °C | |
| Front Temperature | 210 to 250 | °C | |
| Nozzle Temperature | 210 to 250 | °C | |
| Processing (Melt) Temp | < 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 68.6 to 123 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C | |
| Melt Temperature | < 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 TFE 15 | RTP Company | Nylon 66 | RTP |
| Zelux® GS | Westlake Plastics Company | PC | Zelux® |
| Haysite Plastics HTF | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| Kelon® A H CEG/40 | LATI S.p.A. | Nylon 66 | Kelon® A |
| Petrothene® LT523513 | LyondellBasell Industries | HDPE | Petrothene® |