CABELEC® CA3899
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Cabot Corporation |
| Trademark: | CABELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dQGElg_CABELEC-CA3899.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CABELEC® 3899 is an electrically conductive compound based on carbon black and a polyacetal copolymer. Its electrical properties are permanent and are not dependent on atmospheric conditions. The compound can easily be processed on conventional molding equipment. CABELEC 3899 is principally recommended for applications where freedom from the hazard of electrostatic discharge is requested. Examples of use are in handling of explosive powders, pigments, liquids and electronic components. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.39 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) 2 | ISO 1133 | ||
| 190°C/10.0 kg | 28 | g/10 min | |
| 190°C/2.16 kg | 3.0 | g/10 min | |
| 190°C/5.0 kg | 9.3 | g/10 min | |
| Molding Shrinkage - Flow 3 | 1.5 to 2.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 4(Shore D, 15 sec) | 79 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 5 | ISO 527-2 | ||
| Yield | 45.7 | MPa | |
| Break | 45.2 | MPa | |
| Tensile Strain 6(Break) | 42 | % | ISO 527-2 |
| Flexural Modulus 7 | 1900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 8(23°C) | 11 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 9(1.8 MPa, Unannealed) | 72.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature 10 | 168 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 11 | 5.0E+2 | ohms | IEC 60093 |
| Volume Resistivity 12 | 39 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 180 | °C | |
| Front Temperature | 180 | °C | |
| Nozzle Temperature | 200 | °C | |
| Mold Temperature | 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | CTM E023 |
| 2 . | CTM E005 |
| 3 . | CTM E047 |
| 4 . | CTM E030 |
| 5 . | CTM E041 |
| 6 . | CTM E041 |
| 7 . | CTM E040A |
| 8 . | CTM E044A |
| 9 . | CTM E038 |
| 10 . | CTM E039 |
| 11 . | CTM E042E |
| 12 . | CTM E043B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-IM-G40 | Polymer Resources Ltd. | Nylon 66 | PRL |
| RTP 1008 | RTP Company | PBT | RTP |
| Complet® LGF60-PP | PlastiComp, Inc. | PP Homopolymer | Complet® |
| Grivory® GV-4 FWA black 9225 | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| KEBATER® PBT BM240 | BARLOG plastics GmbH | PBT | KEBATER® |