Sarlink® TPE ME-2570B XRD
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dPsGXh_Sarlink-TPE-ME-2570B-XRD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink ME-2500 Series are high-flow injection molding materials with excellent UV resistance and adhesion to glass. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A, 1 sec | 73 | ISO 868 | |
| Shaw A, 5 seconds | 70 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Flow : 100% strain, 23°C | 2.20 | MPa | ISO 37 |
| Transverse flow : 100% strain, 23°C 1 | 2.05 | MPa | ISO 37 |
| Tensile Strength | |||
| Flow : fracture, 23°C | 5.90 | MPa | ASTM D412 |
| Transverse flow : fracture, 23°C 2 | 6.50 | MPa | ISO 37 |
| Tensile Elongation | |||
| Flow : fracture, 23°C | 730 | % | ASTM D412 |
| Transverse flow : fracture, 23°C 3 | 800 | % | ISO 37 |
| Tear Strength | ISO 34 | ||
| Flow : 23°C | 28 | kN/m | ISO 34 |
| Transverse flow : 23°C, 500mm 4 | 28 | kN/m | ISO 34 |
| Compression Set (70°C, 22 hr) | 43 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | ISO 188 | ||
| 110°C, 1008 hr | -10 | % | ISO 188 |
| 125°C, 1008 hr | -23 | % | ISO 188 |
| Changes in tensile stress upon fracture in air- Transverse flow | ISO 188 | ||
| 110°C, 1008 hr | -5.0 | % | ISO 188 |
| 125°C, 1008 hr | -8.0 | % | ISO 188 |
| Change in Shore Hardness in Air | ISO 188 | ||
| Support a, 110°C, 1008 hr | 3.3 | ISO 188 | |
| Support a, 125°C, 1008 hr | 4.5 | ISO 188 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, 206 1/sec (200°C) | 134 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 175 - 195 | °C | |
| Front Temperature | 180 - 205 | °C | |
| Nozzle Temperature | 180 - 205 | °C | |
| Processing (Melt) Temp | 180 - 205 | °C | |
| Mold Temperature | 15.0 - 40.0 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 176°F (80°C). |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex NT0620GB | Ginar Technology Co., LTD. | Nylon 6 | Mapex |
| TABOREN EC 59 C 50 | SILON s.ro | LLDPE | TABOREN |
| Accura® Xtreme™ | 3D Systems | Unspecified | Accura® |
| Alpha PVC GM 8017 NATURAL | AlphaGary | PVC, Unspecified | Alpha PVC |
| LNP™ STAT-KON™ OE006A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ STAT-KON™ |