EPO-TEK® T905BN-3
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dOmA0Z_EPO-TEK-T905BN-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® T905BN-3 is a thermally conductive, electrically insulating epoxy designed for heat sinking and encapsulation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 300 | µm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 347 | °C | TGA |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 4.97 | GPa | |
| Thixotropic Index | 1.53 | ||
| Weight Loss on Heating | |||
| 200°C | < 0.050 | % | |
| 250°C | 0.16 | % | |
| 300°C | 1.0 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 40.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 3.7E-5 | cm/cm/°C | |
| -- 3 | 1.5E-4 | cm/cm/°C | |
| Thermal Conductivity | 2.0 | W/m/K |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 14 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 4 | Clear/Transparent | ||
| -- 5 | Grey | ||
| Density | |||
| Part B | 0.958 | g/cm³ | |
| Part A | 1.65 | g/cm³ | |
| Viscosity 6(23°C) | 2.0 to 7.0 | Pa·s | |
| Curing Time (80°C) | > 2.0 | hr | |
| Pot Life | 180 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 60 | ||
| Lap Shear Strength (23°C) | > 11.0 | MPa | |
| Relative Permittivity (1 kHz) | 3.51 | ||
| Volume Resistivity (23°C) | 3.0E+11 | ohms·cm | |
| Dissipation Factor (1 kHz) | 9.0E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 50 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene M30P100-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Titalon® 1100CF | Titan Plastics Compounds Co., Ltd. | Nylon 6 | Titalon® |
| Andur 9500-AP/Curene® 185 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Lustran® SAN CN20 | Styrolution | SAN | Lustran® SAN |
| POCAN® B 3235 XF 000000 | LANXESS GmbH | PBT | POCAN® |