PA 6, 15 % glass fibers, blow molding, improved impact strength, heat-aging stabilized

General Information
Filler / Reinforcement	Glass fiber reinforced material, 15% filler by weight
Additive	heat stabilizer
Features	Impact resistance, good Good heat aging resistance
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Blow molding

Physical	Dry	Conditioned	Unit	Test Method
Density (23°C)	1.20	--	g/cm³	ISO 1183
Apparent Density	0.70	--	g/cm³	ISO 60
Molding Shrinkage				ISO 294-4
Vertical flow direction : 280°C, 2.00mm ¹	0.60	--	%	ISO 294-4
Vertical flow direction : 120°C, 2 hours, 2.00mm ²	0.10	--	%	ISO 294-4
Flow direction : 280°C, 2.00mm ³	0.90	--	%	ISO 294-4
Flow direction : 120°C, 2 hours, 2.00mm ⁴	0.20	--	%	ISO 294-4

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	140	--	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	5300	2500	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	105	55.0	MPa	ISO 527-2/5
Tensile Strain (Break, 23°C)	5.0	19	%	ISO 527-2/5
Flexural Modulus ⁵(23°C)	4800	2300	MPa	ISO 178/A
Flexural Stress ⁶
3.5% strain	150	55.0	MPa	ISO 178/A
23°C	165	75.0	MPa	ISO 178
Flexural Strain at Flexural Strength ⁷(23°C)	5.5	7.5	%

Flammability	Dry	Conditioned	Unit	Test Method
Burning Behavior ⁸	passed	--		ISO 3795

Additional Information	Dry	Conditioned		Test Method
ISO Shortname	PA 6-HI, BHR, 14-050, GF15	--		ISO 1874

Injection	Dry	Unit	Test Method
Residual Moisture Content	0.0 - 0.060	%	Karl Fisher

Films	Dry	Conditioned	Unit	Test Method
Film Puncture Energy				ISO 6603-2
-- ⁹	2.50	--	J	ISO 6603-2
-- ¹⁰	4.90	--	J	ISO 6603-2
Film Puncture Force				ISO 6603-2
-- ¹¹	630	--	N	ISO 6603-2
-- ¹²	1200	--	N	ISO 6603-2

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	< 10	10	kJ/m²	ISO 179/1eA
23°C	15	30	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	85	90	kJ/m²	ISO 179/1eU
23°C	80	110	kJ/m²	ISO 179/1eU
Notched Izod Impact				ISO 180/1A
-30°C	10	< 10	kJ/m²	ISO 180/1A
23°C	15	30	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength				ISO 180/1U
-30°C	70	65	kJ/m²	ISO 180/1U
23°C	65	95	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	210	--	°C	ISO 75-2/B
1.8 MPa, not annealed	175	--	°C	ISO 75-2/A
8.0 MPa, not annealed	58.0	--	°C	ISO 75-2/C
Melting Temperature ¹³	221	--	°C	ISO 11357-3
Linear thermal expansion coefficient				ISO 11359-2
Flow : 23 to 55°C	4.0E-5	--	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	1.3E-4	--	cm/cm/°C	ISO 11359-2

Electrical	Dry	Conditioned	Unit	Test Method
Comparative Tracking Index (Solution A)	375	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
1.60 mm	HB	--		UL 94
3.20 mm	HB	--		UL 94

Injection	Dry	Unit	Test Method
Drying Temperature - Dry Air Dryer	80.0	°C
Drying Time - Dry Air Dryer	2.0 - 6.0	hr
Processing (Melt) Temp	270 - 290	°C
Mold Temperature	80.0 - 120	°C

Note Message
1 .	60x60x2; MT 80°C; 600 Bar
2 .	60x60x2
3 .	60x60x2; MT 80°C; 600 Bar
4 .	60x60x2
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	Pull Rate: 2 mm/min; 50% RH
8 .	US-FMVSS302
9 .	-30°C
10 .	23°C
11 .	-30°C
12 .	23°C
13 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Spartech Polycom SC1-6010	Spartech Polycom	ABS	Spartech
LNP™ LUBRICOMP™ JCL36E compound	SABIC Innovative Plastics	PESU	LNP™ LUBRICOMP™
PHOENIX™ 1081	Phon Tech Industrial Company	SBC	PHOENIX™
Plaskon MUF-LFG	Cookson Electronics - Semiconductor Products	Epoxy	Plaskon
LNP™ LUBRICOMP™ JFL36 compound	SABIC Innovative Plastics	PESU	LNP™ LUBRICOMP™