Novalloy-B B5546 (Type D)
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dNHZgU_Novalloy-B-B5546-Type-D-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Novalloy-B B5546 (Type D) is an Acrylonitrile Butadiene Styrene + PBT (ABS+PBT) material filled with 30% glass fiber. It is available in Asia Pacific. Important attributes of Novalloy-B B5546 (Type D) are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 110 | MPa | ISO 527-2 |
| Flexural Modulus | 9500 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 6.40 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 210 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 150 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 145 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 2.0E-5 | cm/cm/°C | |
| Transverse | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (1.5) | 27 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) (1.50 mm) | 19.0 | UL 746 | |
| High Amp Arc Ignition (HAI) (1.50 mm) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | 208 | mm/min | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) (1.50 mm) | 31 | sec | UL 746 |
| Hot-wire Ignition (HWI) (1.50 mm) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PRC25TF3.2-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Grupo IDESA HIPS HI-760-L-01 | Grupo IDESA, S.A. de C.V. | SBC | Grupo IDESA HIPS |
| ESTABLEND PC ABS 4501 V0 | Cossa Polimeri S.r.l. | PC+ABS | ESTABLEND |
| Kazan HDPE 293-284 | Kazanorgsintez Joint Stock Company | HDPE | Kazan HDPE |
| TECHNYL® A 238 V13 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |