CYCOLAC™ EX39F resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dN38QK_CYCOLAC-EX39F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Highest impact extrusion ABS for sheet and blow molding applications. FDA food contact compliant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 - 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1680 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 35.9 | MPa | ASTM D638 |
| Fracture | 29.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 3.5 | % | ASTM D638 |
| Fracture | 110 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 1900 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 57.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 320 | J/m | ASTM D256 |
| 23°C | 460 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 39.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 91.7 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 77.8 | °C | ASTM D648 |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.2E-4 | cm/cm/°C | ASTM E831 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (240°C, 100 sec^-1) | 1520 | Pa·s | ASTM D3835 |
| Extrusion instructions |
|---|
| Extrusion Blow Molding Parameters: Adapter - Zone 5 Temperature: 193 - 221 C Barrel - Zone 1 Temperature: 188 - 221 C Barrel - Zone 2 Temperature: 188 - 221 C Barrel - Zone 3 Temperature: 188 - 221 C Barrel - Zone 4 Temperature: 188 - 221 C Die Temperature: 193 - 221 C Drying Temperature: 82 - 88 C Drying Time: 5 - 4 hrs Drying Time (Cumulative): 24 hrs Extruder Feed Zone Temperature: 60 - 79 C Head - Zone 6 - Top Temperature: 193 - 221 C Head - Zone 7 - Bottom Temperature: 193 - 221 C Maximum Moisture Content: .02 - .04 % Melt Temperature (Parison): 210 - 227 C Minimum Moisture Content: .04 % Mold Temperature: 38 - 88 C Screw Speed: 20 - 60 rpm Sheet Extrusion Parameters: Adapter Temperature: 199 - 227 C Barrel - Zone 1 Temperature: 193 - 210 C Barrel - Zone 2 Temperature: 199 - 221 C Barrel - Zone 3 Temperature: 204 - 232 C Barrel - Zone 4 Temperature: 210 - 235 C Die Temperature: 210 - 241 C Drying Temperature: 88 - 93 C Drying Time: 2 - 4 hrs Maximum Moisture Content: .001 % Melt Temperature: 210 - 241 C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radiflam® A RV250K AE 121 C NAT 3489 | Radici Plastics | Nylon 66 | Radiflam® |
| Telcar® TL-1120E | Teknor Apex Company | TPE | Telcar® |
| VESTOLIT® E 6507 | VESTOLIT GmbH & Co. KG | PVC, Unspecified | VESTOLIT® |
| G-Lene W50A009 | Gas Authority of India Limited | HDPE | G-Lene |
| Sylvin 8773-60D Brown 7372 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |