LNP™ LUBRICOMP™ GX07409H compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dMFLr1_LNP-LUBRICOMP-GX07409H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP GX07409H is a compound based on PSU resin containing proprietary fillers. Added features of this grade include: Wear Resistant, Healthcare. Also known as: LNP* LUBRICOMP* Compound GX07409H Product reorder name: GX07409H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.51 to 0.71 | % | |
| Across Flow : 24 hr | 0.63 to 0.83 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2520 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 68.0 | MPa | |
| Break | 48.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 5.8 | % | |
| Break | 9.3 | % | |
| Flexural Modulus 1 | 2640 | MPa | ISO 178 |
| Flexural Stress | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 220 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 167 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 to 338 | °C | |
| Middle Temperature | 338 to 349 | °C | |
| Front Temperature | 349 to 360 | °C | |
| Processing (Melt) Temp | 360 to 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 3101-15 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| SEETEC LLDPE UR754 | Lotte Chemical Corporation | LLDPE | SEETEC LLDPE |
| Telcar® TL-1424A | Teknor Apex Company | TPE | Telcar® |
| Tarnamid® T- 30 MHLS | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Kepital® F20-33 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |